Product:Пластик ПВХ вспененный листовой

PVC foam board is an ideal CNC cutting material, it can be used to cut cabinet boards, hollow carving to make decorative partitions, and can also be cut into art letters.




Place of Origin:Shandong, China

Properties Units Average Result
Thickness mm 1~40
Width mm 1220, 1560, 2050
Length mm 2440, 3050
Apparent density g/cm³ 0.3-1.0
Determination of Water Absorption % 0.19
Tensile Strength at Yield MPa 19
Elongation at Break % 16
Flexural Modulus GPa 0.9
Charpy Impact Strength KJ/m² 1.4
Shore D Hardness Value 50
Pulling strength MPa 12
Bending strength MPa 20
Compressive strength MPa 4

Features :

Light-weight, easily transported and processed;
Smooth and easily printed and filmed with kinds of colors.
Good plasticity, excellent thermoforming material;
High Impact and fireproof;
Anti-chemical corrosion, Non-toxic;
Water-proof and good heat preservation;
Good sound insulation and shock absorption;
Unfading and anti-aging
Many ways of processing such as drilling, sawing ,nailing, planing, cementing, jointing.etc.

Advertisement: silk screen printing, engraving materials, exhibition board,denoters;
Building & Decoration: decorative sheets for outdoors and indoors, storage racks, room segments;
Vessel&Vehicle: interior decorating materials of buses, train, subway, steamships, airplane;
Furniture: office furniture, kitchen cabinet, bathroom cabinet;
Industrial Application: thermoformed products, refrigeratory warehouse project, environmental prot ection engineering;
Others: moulding board, sports apparatus, breeding timber, beach moisture-proof facilities, water-resistant timber, art materials, all kinds of light partition plates.

Delivery Port:Qingdao port
Delivery Time:Qty for 1x20ft container 10-15 days
Qty for 1x20ft container 15-21 days


Bulk Density 0.3-1.0 g/cm3 Dimensional Stability ±2%
Shore Hardness 30-85 D Water Absorption <1%
Tensile Strength 12-20 Mpa Flexural Strength 12-18 Mpa
Elongation At Break 15-20% Flexural Modulus 800-900 Mpa
Impact Strength 8-15 KJ/m2 Screw Holding Strength >800 N
Vicat Softening Temperature 73-76 ℃ Heating Dimensional Variation Ratio +2%
Hydroscopicity ≤1% Fire Resistance self-extinguish within 5 seconds